Incoloy 925 round bars bolts and nuts fasteners

Model NO.: Incoloy 925


Standard: JIS, GB, DIN, BS, ASTM, AISI


Type: Nickel Bar


surface: bright or black


Trademark: ToLand Alloy


Origin: China




Application: Aviation, Electronics, Industrial, Medical, Chemical


Alloy: Alloy


Powder: Not Powder


length: random, fixed


Specification: 6-300mm


HS Code: 7222


High Performance Incoloy 925 / UNS N09925 Nickel Alloy Round Bar ASTM B805:

Delivery Time:25-30 days

Certification:CE,FCC,MSDS

Incoloy 925 / UNS N09925 Nickel Alloy Round Bar ASTM B805

1. Grade: Incoloy 925

2. Process: VIR - VAR - ESR - Forging - Semifinished - Finished

3. Delivery Condition: Forged, Solution Annealed, Aged

4. Surface Condition: Black, Machining

5. OD: 6-500mm

6. Specification: ASTM, ASME, GB, JIS, GOST, DIN, etc.

7. Packing: Plywood case, Bundle



General Characteristics of Incoloy 925

Incoloy 925 is a precipitation-hardenable nickel-iron-chromium alloy. It combines high strength with Incoloy 825's excellent corrosion resistance. Incoloy 925 is particularly resistant to sulfide-induced stress cracking and stress-corrosion cracking.



Chemical Composition of Incoloy 925

%	Ni	Fe	Cr	C	Mn	Si	P	S	Mo	Cu	Ti	Al	Nb
min	42.0	22.0	19.5						2.5	1.5	1.9	0.10
max	46.0		22.5	0.030	1.00	0.50	0.030	0.030	3.5	3.0	2.4	0.50	0.50

Physical properties

Density	8.08 g/cm3
Melting range	1311-1366ºC

Heat Treatment of Incoloy 925

Anneal by holding at 1800°F (982°C) for ½ to 1 hour, then rapidly cool (air cool small sections, water quench others) Aging Heat to 1400°F (760°C) Hold at temperature 8 hours Furnace cool at 100°F (38°C) per hour Hold at 1150°F (621°C) for 8 hours Air cool

Applications of Incoloy 925

Oil industry, including tool joints, tubular products, and parts for intermediate sour-gas wells Fasteners Pump and marine shafting Strong, seamless piping and tubing

Machinability of Incoloy 925

Perform on hot-worked metal suggested to provide best finish while conserving machining

Workability of Incoloy 925

Hot working Similar to Incoloy 825 up to 2000°F (1093°C) - higher temperatures produce a stronger, less-ductile metal 1600° to 2150°F (871° to 1177°C) hot working range Perform final hot working from 1600° to 1800°F (871° to 982°C) for top mechanical properties and best corrosion resistance Cold working Higher work-hardening rate than Incoloy 825

Contact us if you need more details on Incoloy 925. We are ready to answer your questions on packaging, logistics, certification or any other aspects about UNS N09925、Nickel Alloy Round Bar. If these products fail to match your need, please contact us and we would like to provide relevant information.